SLA photopolymer —— PSS-WT078

SLA photopolymer —— PSS-WT078

SLA photopolymer —— PSS-WT078

TECHNICAL DATA (PSS-WT078)

Mechanical properties

ASTM Method

Property Brief Introduction

Metric

D638M

Tensile Strength at Break

53-59 MPa

D638M

Tensile Modulus

2450-2730 MPa

D790M

Flexural Strength

90-106 MPa

D790M

Flexural Modulus

2530-2810 MPa

D638M

Elongation at Break

12-16 %

D638M

Izod Impact (Notched)

35-41 J/cm

D2240

Hardness( Shore D)

80

D648-07

Deflection Temperature

65 ℃

E1545-00

Tg

68 ℃

D955

Volumetric shrinkage

< 2.5%

Din ISO 1183-1

Density

1.120 g/cm3

 

TECHNICAL DATA - LIQUID PROPERTIES AND OPOTICAL PROPERTIES

Appearance

Opaque White

Viscosity

350-500 mPa.s @25℃

Density

1.100g/cm3 @ 25℃

Ec [critical exposure]

10.5 mJ/cm2

Dp [slope of cure -depth vs. In(E) cure]

0.12mm

 

 

Brief Introduction


 PSS-WT078 is an industrial stereolithopgraphy liquid photopolymer used to produce robust, functional and accurate parts.

 This material offers superior chemical resistance , a wide processing latitude and excellent tolerance to broad range of temperatures and humidity.

 PSS-WT078 also offers a good balance of properties between rigidity and functionality.

Note:PSS-WT078 matches printer with 355 nm light wave 

 

Applications


 PSS-WT078 is used in solid imaging processes , like stereolithography, to bulid three - dimensional parts .

 It is also useful in creating parts for applications where durability and robustness are critical requirements.

 

Key benefits   


Excellent mechanical property
Low odor 

Low shrinkage

 

Storage condition


■ Avoid light

■ Storage temperature  8-28 ℃

Note: unused materials should not be put back to bottle